LOCTITE ECCOBOND UF 1175

Harmonization Code : 3907.30.00.90 | Polyacetals, other polyethers and epoxide resins, in primary forms; polycarbonates, alkyd resins, polyallyl esters and other polyesters, in primary forms : Epoxide resins : Other

Main features

White
Low CTE
Easy dispensability

Product Description

LOCTITE ECCOBOND UF 1175 partial, white epoxy underfill is formulated for use on large chip sizes, providing good UPH and reliability. Typically used as an electronics encapsulant and a circuit board underfill

LOCTITE ECCOBOND UF 1175 is a fast cure, monocomponent underfill with controlled flow. It offers low CTE and can be dispensed easily and without stringing.

Cure Schedule

15 minutes @ 120°C

Specifications

Technical Specifications

General Properties

Shelf Life Shelf Life Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties. It differs vastly per product and it is based on temperature and storage conditions. The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ -20°C	183 days

Specific Gravity

Specific Gravity
Specific gravity (SG) is the ratio of the density of a substance to the density of a reference substance; equivalently, it is the ratio of the mass of a substance to the mass of a reference substance for the same given volume.

For liquids, the reference substance is almost always water (1), while for gases, it is air (1.18) at room temperature. Specific gravity is unitless.

1.65

Physical Properties

Thixotropic index

Thixotropic index
Thixotropic Index is a ratio of a material s viscosity at two different speeds in Ambient temperature, generally different by a factor of ten.

A thixotropic material s viscosity will decrease as agitation or pressure is increased. It indicates the capability of a material to hold its shape. Mayonnaise is a great example of this. It holds its shape very well, but when a shear stress is applied, the material easily spreads.

It helps in choosing a material in accordance to the application, dispense method and viscosity of a material.

1.05

Viscosity

Viscosity
Viscosity is a measurement of a fluid’s resistance to flow.

Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.

A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
water would.

The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application

35,295 mPa.s

Mechanical Properties

Storage (DMA) Modulus
Storage (DMA) Modulus @ 25°C	13,984 N/mm2

Thermal Properties

Coefficient of Thermal Expansion (CTE) Coefficient of Thermal Expansion (CTE) CTE (Coefficient of thermal expansion) is a material property that is indicative of the extent to which a material expands with a change in temperature. This can be a change in length, area or volume, depending on the material. Knowing the CTE of the layers is helpful in analyzing stresses that might occur when a system consists of an adhesive plus some other solid component.
Coefficient of Thermal Expansion (CTE), α1 Coefficient of Thermal Expansion (CTE), α1 CTE α1 (alpha 1) is the slope of the Coefficient of thermal expansion in a temperature range below the Glass transition temperature (Tg). It explains how much a material will expand until it reaches Tg.	19 ppm/°C
Coefficient of Thermal Expansion (CTE), α2 Coefficient of Thermal Expansion (CTE), α2 CTE α2 (alpha 2) is the slope of the Coefficient of thermal expansion in a temperature range above the Glass transition temperature (Tg). It explains the extent to which a material will expand after it passes Tg.	68 ppm/°C

Glass Transition Temperature (Tg)

Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.

154 °C