OP-216 | Nano-Scale Adhesion-Promoting Surface Treatment


Main features
  • Improved adhesion strength of paints/coatings on metal surfaces
  • No outgassing
  • No stress build-up on the substrates

Product Description

OP-216 nano-scale coating product is a surface treatment capable of promoting adhesion on most metal surfaces. It can be applied via most traditional coating processes, including dipping, spraying, wiping, etc.

OP-216 is designed to improve adhesion for coatings that cross-link with carboxylic acid functional groups (e.g. epoxies, melamine-formaldehyde, etc.).

Product Family
OP-216  
240ml bottle

Catalog Product

Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.
Shipping in 4 - 6 weeks Shipping in 4 - 6 weeks Shipping in 4 - 6 weeks
Packaging
TDS, SDS & Technical documents

Technical Specifications

General Properties
Color
Color
The color
 Clear
Shelf Life
Shelf Life
Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties.

It differs vastly per product and it is based on temperature and storage conditions.

The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ 25°C 730 days
Physical Properties
Viscosity
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow.

Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.

A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
water would.

The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application
 2 mPa.s
Electrical Properties
Visible Light Transmission 100 %
Thermal Properties
Boiling Point
Boiling Point
The amount of degree’s needed to reach in order to make the substance boil.
 82 °C

Additional Information

Surface Preparation/ Cleaning:
Ensure that the surface is free of any grease, fingerprints or dirt (i.e., water break free). This can be accomplished by first degreasing the surface with solvents or by rinsing with soap and water. The next step is to remove monolayer-scale contaminants. This is typically performed by using a cleaner specifically designed for the metal you are working with. Contact Aculon if you are unsure what cleaner to use and we will recommend one best suited for your application. The substrate should be water break - free before continuing to coating steps.

Treatment Application:
Spray: Spray the solution onto the substrate using doubl e passes. Post-application curing is
recommended for best performance. Spray Equipment Suggestions: HVLP (Binks Mach 1), HVLP
(Devilbiss JGHV), Air Atomizatation (Devilbiss MBC gun), and Airless (Graco Model 225-292 President
Pump Series A)

Dip: – Immerse the substrate in the solution for five minutes. If a shorter dip time is necessary, then a
post-cure is recommended for optimal performance (sonication while dipping can boost performance in
some cases).

Dip Coating with Sonication: Ensure the substrate is clean. Completely submerge the substrate in the
solution and sonicate for five minutes. Remove substrate from the solution and allow to air dry , preferably
in a clean area.

Drying/ Curing: If curing is necessary (short dip times or spray-application), the treated substrates are
best cured at 120C peak metal temperature for approximately 30 seconds. For silicon and titanium
oxides, lengthening the cure time to 5 minutes is recommended.
*Note: If OP-225 is being used to adhere a high viscosity or low-reactive resin system, especially if such coating is
not cured after application, then it is suggested to do a post cure rinsing step (or post-treatment rinse if curing was not
performed) for best performance. Furthermore, if a UV-curable coating system is being used, then it may be
necessary to modify the curing parameters to ensure sufficient radical generation near the surface of the monolayer
to achieve optimal adhesion. In certain cases it is also possible to directly blend the active materials into a coating;
contact an Aculon representative if this approach is of interest to you.

Safety, Handling, Storage, Shelf Life:
Store in a cool (~25C) and dry area, and keep away from direct sun light. See this product’s MSDS for
proper handling and fire hazard data. When stored properly, product has a 2 year shelf life from the date
it is opened.